乙烯-甲基丙烯酸甲酯共聚物對聚氯乙烯／聚丙烯復合材料性能的影響 |
| 楊 治1，李志軍1，莫笑君1，劉 滔1，蘇勝培1*，歐陽(yáng)湘會(huì )2，張 芳2，周乃安2
（1. 湖南師范大學(xué) 化學(xué)化工學(xué)院，湖南 長(cháng)沙 410081；2. 湖南五強產(chǎn)業(yè)集團股份有限公司 新型材料分公司，湖南 長(cháng)沙 410205） |
| 摘 要：以乙烯-甲基丙烯酸甲酯共聚物（EMMA）為增容劑制備了聚氯乙烯（PVC）／聚丙烯（PP）復合材料，采用DSC表征了復合材料的相容性，用WDW3020微控電子萬(wàn)能實(shí)驗機、XCJ-40電子沖擊實(shí)驗機測試了復合材料的力學(xué)性能；并與氯化聚乙烯（CPE）增容PVC／PP共混體系進(jìn)行了比較。試驗結果表明：EMMA能顯著(zhù)改善PVC與PP的相容性。當增容劑用量為9份時(shí)，與未增容PVC／PP體系相比，缺口沖擊強度，拉伸強度和彎曲強度分別提高了191%，70%，41%；與CPE增容PVC／PP體系相比，缺口沖擊強度，拉伸強度和彎曲強度分別提高了44%，39%，12%。 |
| 關(guān)鍵詞：乙烯-甲基丙烯酸甲酯共聚物（EMMA）；聚氯乙烯；聚丙烯；力學(xué)性能 |
| 中圖分類(lèi)號：TQ050.4+3 文獻標識碼：A 文章編號：1009-9212（2009）05- 0056-05 |
|
| Effect of Ethylene-MMA co-Polymer on the Properties of PVC／PP Composites |
| YANG Zhi1，LI Zhi-jun1，MO Xiao-jun1，LIU Tao1，SU Sheng-pei1*，OUYANG Xiang-hui2，ZHANG Fang2，ZHOU Nai-an2
（1.College of Chemistry and Chemical Engineering，Hunan Normal University，Changsha 410081，China；2. Hunan Wuqiang Corporation Group New Materials Branch，Changsha 410205，China） |
| Abstract：PVC／PP composites using ethylene-MMA co-polymer（EMMA）as the compatibilizer were prepared. The compatibility of PVC／PP composites were characterized by means of different scanning calorimeter（DSC）. The mechanical properties of PVC／PP composites were tested using WDW3020 electronic universal testing machine and XCJ-40 electronic impact testing machine. Furthermore，the difference between EMMA and chlorinated polyethylene（CPE）as compatibilizer for PVC／PP composites was also investigated. The experimental results have shown that the compatibility between PVC and PP were apparently improved due to the addition of EMMA. Compared with pure PVC／PP composites，when 9 phr EMMA were added，the notch impact strength，tensile strength and flexural strength of PVC／PP composites were improved by 191%，70% and 41%，respectively. Whereas compared with PVC／PP composites using CPE as compatibilizer，the notch impact strength，tensile strength and flexural strength were improved by 44%，39% and 12%，respectively. |
| Key words：ethylene-MMA co-polymer（EMMA）；poly（vinyl chloride）；polypropylene；mechanical property |
|